| Caighdeán | Grád | ||||||
|---|---|---|---|---|---|---|---|
| Comhdhéanamh ceimiceach % | |||||||
| C: | Sea: | Mn: | C: | S: | Cr: | ceachtar: | cu: |
| ISO | C90U - 1.1535 | ||||||
| 0.85-0.95 | 0.15-0.3 | 0.15-0.4 | <0.030 | <0.030 | - | - | - |
| DIN | C85W - 1.1830 | ||||||
| 0.8-0.9 | 0.1-0.3 | 0.1-0.35 | <0.030 | <0.030 | - | - | - |
| PN | N9 | ||||||
| 0.85-0.94 | 0.15-0.35 | 0.15-0.35 | <0.030 | <0.030 | <0.2 | <0.25 | <0.25 |
| STAS | OSC 8M | ||||||
| 0.8-0.9 | 0.15-0.35 | 0.35-0.80 | <0.030 | <0.025 | <0.2 | <0.25 | <0.25 |
| GOST | U9A - У9А | ||||||
| 0.85-0.94 | 0.17-0.33 | 0.17-0.28 | <0.025 | <0.018 | <0.2 | <0.25 | <0.25 |
| B.S. | BW1 | ||||||
| 0.85-0.95 | <0.3 | <0.35 | <0.15 | - | <0.15 | <0.2 | - |
| PN | N9E | ||||||
| 0.85-0.94 | 0.15-0.3 | 0.15-0.3 | <0.025 | <0.025 | <0.15 | <0.2 | <0.2 |
Cur síos ar Steels U9A // C85W -
Cruach a bhfuil cion carbóin beagán níos airde ná an pointe eutectoid. Is é an grád cruach é a bhfuil an t-ábhar cóimhiotail is ísle de na steels uirlisí go léir a úsáidtear le haghaidh meaisínithe. Cé go bhfuil cruas aige cosúil le cruas steels le cion carbóin níos airde, tá friotaíocht abrasion níos ísle aige agus ceannródaíocht níos measa. Tá friotaíocht níos mó ag N9E ar thionchar agus turraing ná N9, mar sin moltar cruach N9E a úsáid le haghaidh iarratais a dteastaíonn cáilíocht níos airde orthu.
Feidhmchláir
Úsáidtear an cóimhiotal seo go forleathan le haghaidh: Slisíní Punches Gearrthóirí Uirlisí Adhmaid Scriú sconnaí
Airíonna meicniúla agus fisiceacha
Is é cruas an tréith is tábhachtaí sa chás seo.
| Riail | Céim | HB cruas uasta chomh bog annealed | HB cruas uasta i stát tempered |
|---|---|---|---|
| ISO | TC90 | 207 | - |
| GOST | U9 | 192 | 62 |
| GOST | U9A | 192 | 62 |
| PN | N9 | 197 | 62 |
| PN | N9E | 197 | 62 |
| UNI | C90KU | 207 | 60 |
| B.S. | BW1 | 207 | - |
Airíonna eile:
Cumas teasa sonrach:
| Céim: | N9 | N9E | U9A |
|---|---|---|---|
| Friotaíocht leictreach: | 1.76 μΩ*m | 1.76 μΩ*m | - |
| Dlús: | 7.851g/cm3 | 7.851g/cm3 | 7.81g/cm3 |
| 498 J/kg*K | 498 J/kg*K | - | |
| Comhéifeacht leathnú líneach: | 10.84 (10^6)/OC | 10.84 (10^6)/OC | - |
Fuarú
Tá difríocht idir N9 agus N9E ina chumas cruaithe, mar atá U9 agus U9A. Is steels cruaite domhain iad U9 agus N9, agus is steels cruaite dromchla iad U9A agus N9E. Sa chás seo, tá friotaíocht tionchair níos mó ag steels cruaite dromchla ná a gcomhghleacaithe cruaite domhain.
Méid gráin is mó i briste / doimhneacht hardening i briste, mm
| Teocht [céim] | ||||
|---|---|---|---|---|
| An méid gránach is mó i gcás briste/doimhneacht chruaite i bristeadh gléasta, mm | 760 | 800 | 840 | 880 |
| N9 cruach cruaite domhain | 7/5 | 7/6 | 6/8 | 5/12* |
| N9E Cruach Hardening Dromchla | 7/3 | 7/4 | 7/4 | 7/5 |
AIRD! Is dócha go dtarlóidh scoilteanna cruaite le linn briste.
Cóireáil teasa agus obair phlaisteach
Moltar na paraiméadair seo a leanas le haghaidh oibre agus cóireála teasa
| Cóireáil teasa N9E agus brionnú | ||
|---|---|---|
| Próiseas | Cuisniú | Teocht [céim] |
| Gaibhniú | fuinseog nó gaineamh | 1000-800 céim |
| Annealing bog | ar bith | 680-710 céim |
| Faoiseamh strus | mall | 600-700 céim |
| Fuarú | uisce | 760-780 céim |
| Tempered | aer | 180-300 céim |
Táthú
Níl sé éasca le cruach uirlisí den chineál seo a tháthú, mar sin níor cheart táthú a dhéanamh ach amháin le haghaidh deisiúcháin: ENS 50 B, ENS 15CrB, ENS 18, EN 450 B, EN 600 B, WBEN 280 MoB, EN 350 B.
Soláthraímid an cóimhiotal cruach seo mar
Barraí teorollta Bileoga agus plátaí Stiallacha fuar-rollta Sreanga Barraí agus gaibhneachta brionnaithe